| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 86,6 | 70,0 | 1037 | 78,5 | 55,0 | 599 | ||
| 86,3 | 69,5 | 1017 | 78,2 | 54,5 | 589 | ||
| 86,1 | 69,0 | 997 | 77,9 | 54,0 | 579 | ||
| 85,8 | 68,5 | 978 | 77,7 | 53,5 | 570 | ||
| 85,5 | 68,0 | 959 | 77,4 | 53,0 | 561 | ||
| 85,2 | 67,5 | 941 | 77,1 | 52,5 | 551 | ||
| 85,0 | 67,0 | 923 | 76,9 | 52,0 | 543 | ||
| 84,7 | 66,5 | 906 | 76,6 | 51,5 | 534 | ||
| 84,4 | 66,0 | 889 | 501 | 76,3 | 51,0 | 525 | |
| 84,1 | 65,5 | 872 | 494 | 76,1 | 50,5 | 517 | |
| 83,9 | 65,0 | 856 | 488 | 75,8 | 50,0 | 509 | |
| 83,6 | 64,5 | 840 | 481 | 75,5 | 49,5 | 501 | |
| 83,3 | 64,0 | 825 | 474 | 75,3 | 49,0 | 493 | |
| 83.1 | 63,5 | 810 | 468 | 75,0 | 48,5 | 485 | |
| 82,8 | 63,0 | 795 | 461 | 74,7 | 48,0 | 478 | |
| 82,5 | 62,5 | 780 | 455 | 74,5 | 47,5 | 470 | |
| 82,2 | 62,0 | 766 | 449 | 74,2 | 47,0 | 463 | |
| 82,0 | 61,5 | 752 | 442 | 73,9 | 46,5 | 456 | |
| 81,7 | 61,0 | 739 | 436 | 73,7 | 46,0 | 449 | |
| 81,4 | 60,5 | 726 | 430 | 73,4 | 45,5 | 443 | |
| 81,2 | 60,0 | 713 | 424 | 73,2 | 45,0 | 436 | |
| 80,9 | 59,5 | 700 | 418 | 72,9 | 44,5 | 429 | |
| 80,6 | 59,0 | 688 | 413 | 72,6 | 44,0 | 423 | |
| 80,3 | 58,5 | 676 | 407 | 72,4 | 43,5 | 417 | |
| 80,1 | 58,0 | 664 | 401 | 72,1 | 43,0 | 411 | |
| 79,8 | 57,5 | 653 | 396 | 71,8 | 42,5 | 405 | |
| 79,5 | 57,0 | 642 | 391 | 71,6 | 42,0 | 399 | |
| 79,3 | 56,5 | 631 | 385 | 71,3 | 41,5 | 393 | |
| 79,0 | 56,0 | 620 | 380 | 71.1 | 41,0 | 388 | |
| 78,7 | 55,5 | 609 | 375 | 70,8 | 40,5 | 382 | |
Πίνακας μετατροπής τιμής σκληρότητας σιδηρούχων μετάλλων
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 370 | 70,5 | 40,0 | 377 | 269 | 28,0 | 274 | |
| 365 | 70,3 | 39,5 | 372 | 266 | 27,5 | 271 | |
| 360 | 70,0 | 39,0 | 367 | 263 | 27,0 | 268 | |
| 355 | 38,5 | 362 | 260 | 26,5 | 264 | ||
| 350 | 38,0 | 351 | 257 | 26,0 | 261 | ||
| 345 | 37,5 | 352 | 254 | 25,5 | 258 | ||
| 341 | 37,0 | 347 | 251 | 25,0 | 255 | ||
| 336 | 36,5 | 342 | 248 | 24,5 | 252 | ||
| 332 | 36,0 | 338 | 245 | 24,0 | 249 | ||
| 327 | 35,5 | 333 | 242 | 23,5 | 246 | ||
| 323 | 35,0 | 329 | 240 | 23,0 | 243 | ||
| 318 | 34,5 | 324 | 237 | 22,5 | 240 | ||
| 314 | 34,0 | 320 | 234 | 22,0 | 237 | ||
| 310 | 33,5 | 316 | 232 | 21,5 | 234 | ||
| 306 | 33,0 | 312 | 229 | 21,0 | 231 | ||
| 302 | 32,5 | 308 | 227 | 20,5 | 229 | ||
| 298 | 32,0 | 304 | 225 | 20,0 | 226 | ||
| 294 | 31,5 | 300 | 222 | 19,5 | 223 | ||
| 291 | 31,0 | 296 | 220 | 19,0 | 221 | ||
| 287 | 30,5 | 292 | 218 | 18,5 | 218 | ||
| 283 | 30,0 | 289 | 216 | 18,0 | 216 | ||
| 280 | 29,5 | 285 | 214 | 17,5 | 214 | ||
| 276 | 29,0 | 281 | 211 | 17,0 | 211 | ||
| 273 | 28,5 | 278 | |||||
Σημείωμα:
1. Σκληρότητα Brinell: Χρησιμοποιείται κυρίως για τη μέτρηση της σκληρότητας χυτών, σφυρήλατων, μη σιδηρούχων μεταλλικών εξαρτημάτων, θερμής έλασης μπιγιετών και εξαρτημάτων με ανόπτηση. Το εύρος μέτρησης είναι ≥HB450.
2. Σκληρότητα Rockwell: Η HRA χρησιμοποιείται κυρίως για δείγματα υψηλής σκληρότητας για τη μέτρηση της επιφανειακής σκληρότητας υλικών και επιφανειών με σκληρότητα υψηλότερη από HRC67, όπως τσιμεντωμένο καρβίδιο, νιτρωμένος χάλυβας κ.λπ. Το εύρος μέτρησης είναι HRA>70. Η HRC χρησιμοποιείται κυρίως για τη μέτρηση της σκληρότητας χαλύβδινων μερών (όπως ανθρακούχος χάλυβας, εργαλειοχάλυβας, κράμα χάλυβα κ.λπ.) μετά από σκλήρυνση ή σκλήρυνση. Το εύρος μέτρησης είναι HRC20~67.
3. Σκληρότητα Vickers: χρησιμοποιείται για τη μέτρηση της σκληρότητας λεπτών εξαρτημάτων και εξαρτημάτων χαλύβδινων πλακών και μπορεί επίσης να χρησιμοποιηθεί για τη μέτρηση της σκληρότητας εξαρτημάτων που έχουν σκληρυνθεί επιφανειακά, όπως η ενανθράκωση, η κυάνωση και η νιτρίδωση.
Ώρα δημοσίευσης: 07 Απριλίου 2024